Anhui Haihui Chemical Co., Ltd.--Amino resin

PRODUCTS

haihui chemical

Amino resin

1. Butyl etherified melamine formaldehyde resin

Grade	Etherified alcohol	Solid content％	Viscosity T-4/25	Color Iron-Cobalt	Acid value mgKOH/g	Tolerance	Features and Uses
882	Butanol	60±2	60-120s	≤1	≤2	1:2-7①	Good compatibility, good gloss, good plumpness
882-2	Isobutanol	60±2	80-120s	≤1	≤2	1:2-7①	Fast drying and high hardness
882-2A	Isobutanol	60±3	120-150s	≤1	≤2	1:2-7①	Fast drying and high hardness
885-1	Isobutanol	60±4	80-150s	≤1	≤2	1:2-3.5①	Fast drying, high hardness, low temperature fast drying amino paint
860	Butanol	60±5	40-100s	≤1	≤2	1:5-15①	Good compatibility, improve the gloss of paint film, fresh insulation and aging resistance
872	Butanol	60±2	90-130s	≤1	≤2	1:6-15②	Good compatibility, good gloss
865	Isobutanol	60±2	120-160s	≤1	≤2	1:2.5-5①	Fast drying and high hardness
804	Isobutanol	60±2	100-160s	≤1	≤2	1:5-10①	Good compatibility, good vividness, good thickness resistance, good scratch resistance of paint film, fast drying

①D-40 solvent oil tolerance at 20℃, g/g
②20 ℃ mixed solvent (iso-octane: toluene: decalin = 84:8:8), tolerance. M1/g

2. Butylated urea-formaldehyde resin

Grade	Etherified alcohol	Solid content％	Viscosity T-4/25	Color 铁-钴	Acid value mgKOH/g	Tolerance	Features and Uses
8578	Butanol	60±2	60-120s	≤1	≤1	1:2-7①	Fast drying, good adhesion, mainly used for deep drawing coatings and coil coating ring gas primers
8265	Butanol	60±2	100-150s	≤1	≤2	1:5-10②	Butylated Urea Formaldehyde Resin

3. Methyl etherified amino resin

Grade	Solid content％	Viscosity mpa.s/25℃	Color (Fe-Co colorimetry)	Formaldehyde Content%	Features and Uses
HH-98	≥98	2200-6600	≤1	≤0.5	Fully formaldehyde amino resin, high cross-linking density, less dosage, more balanced flexibility and hardness, strong acid catalysis is required for use, and cross-linking is better. Widely used in coil coatings, UV light curing, automotive and other fields.
HH-80A	80±2	2000-5000	≤1	≤0.6	Special synthesis process, good compatibility, good flexibility, excellent storage stability, a methyl etherified amino resin with excellent versatility
HH-80B	80±2	2000-5000	≤1	≤0.6	Special synthesis process, good compatibility, good flexibility, excellent storage stability, a methyl etherified amino resin with excellent versatility
HH-80C	80±2	2200-6600	≤1	≤0.7	Special synthesis process, good compatibility, good flexibility, excellent storage stability, a methyl etherified amino resin with excellent versatility
HH-80W	80±2	2200-6600	≤1	≤0.6	Special synthesis process, good compatibility, good flexibility, excellent storage stability, a methyl etherified amino resin with excellent versatility

Note: The company's manual is only used as a product introduction, and does not represent the technical guarantee of use. Please refer to the experiment before use.

4. Water-based methyl etherified amino resin

Grade	Solid content％	Viscosity mpa.s/25℃	Color (Fe-Co colorimetry)	Formaldehyde Content%	Features and Uses
HH-80S	80±2	2200-6000	≤1	≤0.6	High imino type, good water solubility, good adhesion to metal
HH-75S	75±2	2200-6000	≤1	≤0.6	High imino type, good water solubility, good adhesion to metal
HH-65S	65±2	2200-6000	≤1	≤0.6	High imino type, good water solubility, good adhesion to metal

Note: The company's manual is only used as a product introduction, and does not represent the technical guarantee of use. Please refer to the experiment before use.